Mechanics of Solids (about journal) Mechanics of Solids
A Journal of Russian Academy of Sciences
 Founded
in January 1966
Issued 6 times a year
Print ISSN 0025-6544
Online ISSN 1934-7936

Russian Russian English English About Journal | Issues | Guidelines | Editorial Board | Contact Us
 


IssuesArchive of Issues2020-1pp.16-21

Archive of Issues

Total articles in the database: 11223
In Russian (Èçâ. ÐÀÍ. ÌÒÒ): 8011
In English (Mech. Solids): 3212

<< Previous article | Volume 55, Issue 1 / 2020 | Next article >>
A.D. Berezner, T.N. Pluzhnikova, V.A. Fedorov, D.Yu. Fedotov, and A.V. Yakovlev, "Behaviour of Metallic Glasses under Local Loading and after External Action," Mech. Solids. 55 (1), 16-21 (2020)
Year 2020 Volume 55 Number 1 Pages 16-21
DOI 10.3103/S0025654420010057
Title Behaviour of Metallic Glasses under Local Loading and after External Action
Author(s) A.D. Berezner (Derzhavin Tambov State University, Tambov, 392000 Russia)
T.N. Pluzhnikova (Derzhavin Tambov State University, Tambov, 392000 Russia)
V.A. Fedorov (Derzhavin Tambov State University, Tambov, 392000 Russia, fedorov@tsutmb.ru)
D.Yu. Fedotov (Derzhavin Tambov State University, Tambov, 392000 Russia)
A.V. Yakovlev (Derzhavin Tambov State University, Tambov, 392000 Russia)
Abstract To determine the cracking susceptibility for amorphous metal alloys (AMAs) or metallic glasses, a method based on the determining the dependence of the relative crack resistance (χ) on the load applied to intender of PMT-3 microhardness tester is proposed. In the method, the relative crack resistance at a load of 160 g is set equal to unit. At lower loads, crack resistance has been determined as the average of 10 measurements. In this article, we also have proposed a method for determining the heating temperature of AMA ribbons during laser beam machining that is based on a comparison of the dependence of the relative crack resistance of AMAs on load applied to indenter for samples annealed in the furnace and after laser irradiation. It has been found that cracks begin to appear in the samples after a ten-minute annealing at Ò=773 K.

Fatigue tests of samples under a load varying from a maximum value of 750 MPa to a minimum of 400 MPa under a condition of repeated stress cycle with a frequency of 2 Hz have been carried out using a specially designed setup. In the domain exposed to laser radiation, four characteristic areas can be distinguished on the sample surface: internal reflow zone; dendritic growth area; area with unfinished growth of dendrites, area not exposed to radiation. In these areas, the relative crack resistance (χ) determined via the critical stress intensity factor of the first kind K1c monotonically decreases from 1 in the center to 0 at the periphery. It has been established that the laser action does not affect fatigue, the fatigue limit of the samples remains the same and is equal to 428 MPa. The characteristic features of the destruction are revealed. Cracks that propagate with branching in the reflow zone and after passing through its boundary develop rectilinearly have been found.
Keywords metallic glass, laser radiation, relative crack resistance, fatigue
Received 12 August 2019Revised 22 August 2019Accepted 18 September 2019
Link to Fulltext
<< Previous article | Volume 55, Issue 1 / 2020 | Next article >>
Orphus SystemIf you find a misprint on a webpage, please help us correct it promptly - just highlight and press Ctrl+Enter

101 Vernadsky Avenue, Bldg 1, Room 246, 119526 Moscow, Russia (+7 495) 434-3538 mechsol@ipmnet.ru https://mtt.ipmnet.ru
Founders: Russian Academy of Sciences, Ishlinsky Institute for Problems in Mechanics RAS
© Mechanics of Solids
webmaster
Rambler's Top100